PERFORMANCE DATA |
|
Style
1117
|
|
Black chloroprene rubber with one ply of cotton fabric inserted into the middle of the sheet.
Applications
Recommended for use as diaphragms, gaskets, regulators, control valves, and other static
and dynamic applications. Excellent for petroleum oil service. Other applications include
water, hydrocarbons, salt water, some acids, and general service.
|
TEMPERATURE, MAXIMUM |
-60 to 225°F (-51 to 107°C)
|
| PRESSURE, MAXIMUM |
Diaphragm (1/16"): 300 psi; (2.07 MPa);(21.1 kg/cm²)
Diaphragm (1/8"): 500 psi; (3.45 MPa);(35.2 kg/cm²)
Gasket: 300 psi; (2.07 MPa);(21.1 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
1/16: 315 psi (2.17 MPa) Typical
1/8: 560 psi (3.81 MPa) Typical
|
| TENSILE STRENGTH
(ASTM D412)
|
1100 psi (7.58 MPa) for 1/16", Typical
|
| DENSITY |
6.4 lbs/ft³ (0.1 g/cc) Typical
|
| pH RANGE AT AMBIENT
TEMPERATURE |
4 to 10
|
| DUROMETER,
SHORE "A" ASTM D2240
|
65-75
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 1.25 for 1/16" (1.59 mm) thickness
|
|
"Y" Gasket Factor - 400 psi (2.76 MPa) 1/16" (1.59 mm) thickness
|
Availability
50" (127 cm) wide continuous length in thicknesses of 1/16" (1.59 mm), 1/8" (3.18 mm),
3/16" (4.76 mm), and 1/4" (6.35 mm).
Approximate weight: 3.6 lbs/yd² (1.94 kg/m²) based on a 1/16" (1.59 mm) thick sheet.
|
|
|