PERFORMANCE DATA |
|
Style
1132
|
|
Manufactured from a selected grade of paper that is treated with special resin and bonded
together under high pressure and temperature to form a pliable, yet bone-like hard material.
Applications
Recommended for use in general sealing or gasket applications, and electrical applications.
Suitable for general services including petroleum oils, hydraulic fluids, alcohols,
gasoline, and other hydrocarbon services.
|
TEMPERATURE, MAXIMUM |
225°F (107°C)
|
| PRESSURE, MAXIMUM |
150 psi; (10.3 bar);(1.03 MPa);(10.5 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
N/A
|
| TENSILE STRENGTH
(ASTM D710)
|
8000 psi (55.1 MPa) Crosswise Minimum
14000 psi (96.5 MPa) Lengthwise Minimum
|
| DENSITY |
81.1 lbs/ft³ (1.3 g/cc) Minimum
|
| pH RANGE AT AMBIENT
TEMPERATURE |
4 to 10
|
| DUROMETER,
ROCKWELL ASTM D710
|
R-80
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 1.75 for 1/16"(1.59 mm) thickness
|
|
"Y" Gasket Factor - 1100 psi (76 bar) for 1/16"(1.59 mm) thickness
|
Availability
40"x50" (102x127 cm) and 50"x80" (127x203 cm) sheets with
1/16" (1.59 mm) and 1/8" (3.18 mm)
thicknesses. Coils as narrow as 0.187" (4.76 mm) available.
Approximate weight: 12.3 lbs (5.6 kg) based on a 1/16" (1.59 mm) thickness.
|
|
|