UTEX Industries, Inc. Sheet Packing
|
| |
PERFORMANCE DATA |
|
Style
1160
|
|
Molded or calendered (upon special request) from a 74 durometer high temperature AFLAS® fluoroelastomer compound.
Based on a copolymer of tetrafluoroethylene and propylene.
Applications
Recommended for gasket and other static applications. Has excellent high temperature properties
and resistance to steam. Suitable for most acids, bases, high pH corrosion inhibitors, sour
gas, oils, steam, alcohols, alkalies, polar solvents, and hydrocarbons. Has fair resistance
to aromatic solvents, fuels, ketones, and low molecular weight esters and ethers. Not
suitable for service in chlorinated solvents, Freon refrigerant, and tetrahydrofurane.
|
TEMPERATURE, MAXIMUM |
+32 to 450°F (0 to 232°C)
|
| PRESSURE, MAXIMUM |
275 psi; (19 bar);(1.9 MPa);(19.3 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
N/A
|
| TENSILE STRENGTH
(ASTM D412)
|
2000 psi (13.8 MPa) Typical
|
| DENSITY |
95.5 lbs/ft³ (1.53 g/cc) Typical
|
| pH RANGE AT AMBIENT
TEMPERATURE |
3 to 10
|
| DUROMETER,
SHORE "A" ASTM D2240
|
68-80
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 0.5 for all thicknesses
|
|
"Y" Gasket Factor - 0 psi
|
Availability
Molded: 32"x32" sheets with thicknesses of 1/32" (0.79 mm), 1/16" (1.59 mm),
1/8" (3.18 mm), 3/16" (4.76 mm), and 1/4" (6.35 mm).
Upon special request: Calendered: 36" wide sheets with thicknesses of 1/32" (0.79 mm), 1/16" (1.59 mm),
1/8" (3.18 mm), 3/16" (4.76 mm), and 1/4" (6.35 mm).
Approximate weight: 1.75 lbs (0.8 kg) per sheet based on a 1/32" (0.79 mm) thickness by 32" (81 cm) square.
|
|
|
|
|