UTEX Industries, Inc. Sheet Packing
|
| |
PERFORMANCE DATA |
|
Style
1161
|
|
Molded, or calendered (upon special request), reinforced sheet made from a 74 durometer high temperature AFLAS® fluoroelastomer compound
with nylon cloth insert. AFLAS® based on a copolymer of tetrafluoroethylene and propylene.
Applications
Recommended for gasket and other static applications. Excellent high temperature properties
and resistance to steam. Suitable for most acids, bases, high pH corrosion inhibitors, sour
gas, oils, steam, alcohols, alkalies, polar solvents, and hydrocarbons. Has fair resistance
to aromatic solvents, fuels, ketones, and low molecular weight esters and ethers. Not
suitable for service in chlorinated solvents, Freon refrigerant, and tetrahydrofurane.
|
TEMPERATURE, MAXIMUM |
+32 to 350°F (0 to 177°C)
|
| PRESSURE, MAXIMUM |
400 psi; (27 bar);(2.7 MPa);(28.1 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
430 psi (2.96 MPa) Minimum
|
| TENSILE STRENGTH
(ASTM D751)
|
2880 psi (19.9 MPa) Typical
|
| DENSITY |
95.5 lbs/ft³ (1.53 g/cc) Typical
|
| pH RANGE AT AMBIENT
TEMPERATURE |
3 to 10
|
| DUROMETER,
SHORE "A" ASTM D2240
|
80
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 0.5 for all thicknesses
|
|
"Y" Gasket Factor - 0 psi
|
Availability
Molded: 32"x32" sheets with thicknesses of 1/32" (0.79 mm), 1/16" (1.59 mm),
1/8" (3.18 mm), 3/16" (4.76 mm), and 1/4" (6.35 mm).
Upon special request: Calendered: 36" wide sheets with thicknesses of 1/32" (0.79 mm), 1/16" (1.59 mm),
1/8" (3.18 mm), 3/16" (4.76 mm), and 1/4" (6.35 mm).
|
|
|
|
|