PERFORMANCE DATA |
|
Style
1164
|
|
65 durometer shore "A" homogeneous polyester polyurethane material that is abrasion resistant
and more durable than rubber sheet materials. Has excellent load bearing capabilities.
Applications
Recommended for use as pads, wear resistant lining, bumpers, and general sealing or gasket
applications. Suitable for general services including water, petroleum oils, air, and
abrasive slurries.
|
TEMPERATURE, MAXIMUM |
-50 to 180°F (-46 to 82°C)
|
| PRESSURE, MAXIMUM |
450 psi; (31 bar);(3.1 MPa);(31.6 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
240 psi (1.65 MPa) Minimum
|
| TENSILE STRENGTH
(ASTM D412)
|
5320 psi (36.7 MPa) Typical
|
| DENSITY |
77.4 lbs/ft³ (1.24 g/cc) Typical
|
| pH RANGE AT AMBIENT
TEMPERATURE |
5 to 10
|
| DUROMETER,
SHORE "A" ASTM D2240
|
60-70
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 0.5 for 1/8" (3.18 mm) thickness
|
|
"Y" Gasket Factor - 0 psi
|
Availability
48"x48" (122x122 cm) sheets with thicknesses of 3/16" (4.76 mm),
1/4" (6.35 mm), 5/16" (7.94 mm)
3/8" (9.53 mm), 1/2" (12.7 mm), 5/8" (15.88 mm),
3/4" (19 mm), and 1" (25.4 mm).
Approximate weight: 6.2 lbs/yd² (2.81 kg/m²) based on a 1/4" (6.35 mm) thick sheet.
|
|
|