PERFORMANCE DATA |
|
Style
1165
|
|
A 95 durometer shore "A" homogeneous polyurethane material that is abrasion resistant and
more durable than rubber sheet materials. Has excellent load bearing capabilities.
Applications
Recommended for use as pads, wear resistant lining, bumpers, and general sealing or gasket
applications. Suitable for general services including water, petroleum oils, air, and
abrasive slurries.
|
TEMPERATURE, MAXIMUM |
-50 to 180°F (-46 to 82°C)
|
| PRESSURE, MAXIMUM |
550 psi; (38 bar);(3.8 MPa);(38.7 kg/cm²)
|
| MULLENS BURST STRENGTH D-751-89 |
>460 psi (3.17 MPa) Minimum
|
| TENSILE STRENGTH
(ASTM D412)
|
7000 psi (48.26 MPa) Typical
|
| DENSITY |
79 lbs/ft³ (1.265 g/cc) Typical
|
| pH RANGE AT AMBIENT
TEMPERATURE |
5 to 10
|
| DUROMETER,
SHORE "A" ASTM D2240
|
88-98
|
| BOLT TORQUE |
|
|
"M" Gasket Factor - 1.0 for 1/8" (3.18 mm) thickness
|
|
"Y" Gasket Factor - 200 psi (1.38 MPa) for 1/8" (3.18 mm) thickness
|
Availability
48"x48" (122x122 cm) sheets with thicknesses of 3/16" (4.76 mm),
1/4" (6.35 mm), 5/16" (7.94 mm)
3/8" (9.53 mm), 1/2" (12.7 mm), 5/8" (15.88 mm),
3/4" (19 mm), and 1" (25.4 mm).
Approximate weight: 6.3 lbs/yd² (2.86 kg/m²) based on a 1/4" (6.35 mm) thick sheet.
|
|
|